ASTM A240 316Ti stainless steel is suitable for household articles (tableware, cabinets, cooking utensils, indoor pipelines, water heaters, boilers and bathtubs in Class 1 and 2), auto parts (windshield wipers,mufflers), medical instruments, architectural decoration, chemicals, chemical industry, food & beverages, agriculture and ship machinery, etc.

It is expeditiously brake or roll surrounded into a variety of parts for applications in the mechanical, basic, and transportation fields. This structure gives these Stainless Steel 316 Plates their characteristic combination of weldability and formability.

316Ti is the addition of titanium into 316 quality stainless steel. If the material is exposed to high temperatures from 550 to 800 ¡ã C for a long time, use 316Ti (1.4571) grade stainless steel. 316Ti stainless steels contain low amounts of titanium. This rate is usually 0.5%. 316Ti grade stainless steels have a longer life time than 304 or 316 stainless steel grades.

Corrosion resistance of these Stainless Steel 316 Perforated Sheets can be enhanced by adding Chromium, Molybdenum and Nitrogen. Fabrication of all 316/316Ti/316L Stainless Steel Coils should be done only with tools dedicated to stainless steel materials, where tooling and work surfaces must be thoroughly cleaned before use.

Because stainless steel is more resistant to corrosion, our products like Alloy 316/316Ti/316L Sheets far outlast carbon steel alternatives.

ASTM A240 316Ti plates shall be made by a hot rolling or cold rolling process depending on buyer‘s requirements. The steel shall be made by the electric-arc furnace usually followed by an electroslag remelting process. The plates shall be provided with solution annealing heat treatment, in which it is soaked in the 1900-2150 degree temperature range followed by a water quench.

To achieve optimum corrosion resistance, subsequent stabilizing heat treatment may be performed. Since chromium carbides dissolve at a lower temperature range than titanium carbides, usually the stabilizing temperature is controlled between 1550-1650¡ãF [845-900¡ãC] at which titanium carbides will precipitate but chromium is still in solution. After soaking in the stabilizing temperature for at least 2 hours, the Type 316Ti plates shall be rapidly cooled by air.

ASME SA-240/ ASTM A240 316Ti plates can be used for the construction of pressure vessels according to ASME BPVC Section VIII Division 1 with the minimum and maximum design temperature of -20¡ãF [-29¡ãC] and 1500¡ãF [815¡ãC] respectively. The plates can also be used for the construction of transport tanks according to Section XII with the minimum and maximum design temperature of -20¡ãF [-29¡ãC] and 650¡ãF [343¡ãC] respectively.

HT PIPE is one of the top most manufacturers of?SS 316Ti Plates, which has equivalent corrosion resistance to sensitisation as the low carbon version 316L. ASTM A240 Stainless Steel 316Ti Plates is nonmagnetic in the annealed condition.

ASTM A240 SS 316Ti Plates is commonly utilized in heat exchangers, paper mill equipment, and architectural components in marine environments.?Stainless Steel UNS S31635 Plates?retains physical and mechanical properties similar to standard grades of 316.

304 Stainless Steel Plate has very good formability and can be readily welded by all common methods. 304/304L dual certified.

304 Stainless Plate may become slightly magnetic when worked and is not heat treatable.