ASTM A276 304 420 TP410 Angel A479 316L Round rod steel stainless steel bar

The standard for ASTM A276 specification covers both, hot -finished or cold-finished stainless steel bars with the exception of re-forged bars. The ASTM A276 Type 304 is one of the most commonly used and versatile grades of stainless steel.

Rated 4.5/5 based on 538 customer reviews
Share:
Content

View SS 304 Round Bar at  HT PIPE. Exporter of Durable AMS 5639 Bar and Stainless Steel 304 Rod in China

 

AMS 5639 is the AMS number of the 304 stainless steel. Similarly, the UNS number for this one would be S30400. The specification and standards are the same as that of the ss 304 products. They are available in customizable dimensions, with the same chemical composition. And thus, they can withstand high temperatures and pressures.

 

The ASTM A276 304 Stainless Steel has excellent forming as well as excellent welding characteristics. In fact, the 304 SS Hollow Bar can be welded by all standard fusion techniques, both with and without the use of filler metals. Although, heavy welded sections in the Ss 304 Flat Bar may require a post weld annealing treatment for maximum corrosion resistance.

 

It can be noted that the 304 SS Flat Bar has an excellent performance in a wide range of atmospheric environments as well as many corrosive media. Bars manufactured from grade 304 stainless steel are considered to be resistant to potable water that contains up to about 200 mg/L chlorides at ambient temperatures. the corrosion resistant action of the 304 SS Round Bar reduces to about 150 mg/L at a slightly higher temperature of 60 °C.

 

The Stainless Steel 304 Round Bar is made up of 304 grade stainless steel material. It has around 18% chromium and 8% nickel in its chemical composition. The Stainless Steel 304 Round Bar shows high resistance to corrosion and enhanced strength properties. The material is quite strong with around 515 Mpa min tensile strength and min yield strength of 205 MPa.The 304ss round bars are capable of withstanding high temperatures and high pressures. These bars are also used in pressure vessels as they are capable of retaining their features in a high pressure environment as well. The ss 304 round bars are available in customizable dimensions.

 

The 1.4301 AISI 304 Cold Rolled Bars are made with 304 grade stainless steel and are formed by cold rolling. This is one of the most versatile and widely used stainless steel bars that have 18% chromium and 8% nickel in its chemical composition. This is an austenitic grade ss that can be severely deep drawn. The Stainless Steel 304 Round Bar offers high strength, and good resistance to corrosion, which is why they are used in a wide range of applications.

 

SS 304 Round Bar Chemical Composition

AISI 304 Cold Rolled Bar and SS 304 Rod Stockist in Mumbai, view AMS 5639 Equivalent
Element % Present
Carbon 0.0 – 0.07
Chromium 17.50 – 19.50
Manganese 0.0 – 2.00
Silicon 0.0 – 1.00
Phosphorous 0.0 – 0.05
Sulphur 0.0 – 0.03
Nickel 8.00 – 10.50
Nitrogen 0.0 – 0.11
Fe/ Iron Balance

304 Stainless Steel Bar Mechanical Properties

Manufacturer of 1.4301 Stainless Steel Bar and SUS 304 Polished Bar in Mumbai, check SS 304 Round Bar Price Per Kg in India
Mechanical & Physical Properties Value
Proof Stress MPa 190 Min MPa
Tensile Stress MPa 500 to 700 MPa
Elongation A50 mm Min 45 Min %
Hardness Brinell Max 215 Max HB
Density g/cm³ 8.00 g/cm³
Melting Point ( °C) 1450 °C
Thermal Expansion 17.2 x10^-6 /K
Modulus of Elasticity GPa 193 GPa
Thermal Conductivity W/m.K 16.2 W/m.K
Electrical Resistivity 0.72 x10^-6 Ω .m