Hastelloy B2 2.4617 bolt thread stud bolt DIN976 bolts

Hastelloy Alloys Directory
The Corrosion Resistant HASTELLOY alloys are widely used by the chemical processing industries. The need for reliable performance leads to their acceptance and growth in the areas of energy, health and environmental, oil and gas, pharmaceutical and flue gas desulfurization industries.

This provides greatly enhanced resistance to sulfuric acid. It also has a high chromium content, to maximize its resistance to oxidizing chemicals and process streams contaminated with ferric ions and dissolved oxygen.

It is able to withstand a wide range of oxidizing and non-oxidizing chemicals, and exhibits outstanding resistance to pitting and crevice attack in the presence of chlorides and other halides.

It demonstrates good resistance to neutral and reducing environments. This alloy creates a tenacious oxide, protective film that does not spall off, but it retains superior oxidation resistance at soaring temperatures.

Hastelloy C2000 is available in a variety of sizes and thicknesses, this type of nickel-chromium-molybdenum alloy is renowned for its superior strength and corrosion resistance.

Hastelloy C2000 Tubes are used in a broad range of industries including petrochemical processing, chemical processing equipment manufacturing, oil refineries and power plants.

Hastelloy C2000 lap joint flanges are used for heat treatment applications. They have very little carbon content and high nickel content, which makes them much stronger than any other flanges.

Hastelloy C276 is a nickel-molybdenum-chromium superalloy with an addition of tungsten designed to have excellent corrosion resistance in a wide range of severe environments.Alloy C-276 is one of the most universally corrosion resistant alloys available today. It is used in a variety of environments ranging from moderately oxidizing to strong reducing conditions. Alloy C-276 has exceptional resistance to sulfuric acid, hydrochloric acid, formic acid, acetic acid, chlorides, solvents, wet chloride gas, hypochlorite and chlorine solutions.

These Hastelloy C276 contain a mixture of molybdenum, nickel and chromium species. Like other nickel alloys, it is ductile, easy to form and weld, and has excellent resistance to stress corrosion cracking (a form of easily degradable austenitic stainless steel) in chloride-containing solutions. Due to its high chromium and molybdenum content, it is resistant to oxidizing and non-oxidizing acids and exhibits excellent resistance to pitting and crevice corrosion in the presence of chlorides and other halides.

Hastelloy X Nippo Flange is additionally being offered in customized sizes and shapes to our customers. Hastelloy X Socket Weld Flange is extremely ductile, exhibits excellent weldability, and is definitely fabricated into industrial components. Hastelloy X Ring Joint Type Flange is a fully austenitic advanced corrosion-resistant alloy that gives resistance to both aqueous corrosion and attack at elevated temperatures. Hastelloy X Flanges has greater thermal stability than Hastelloy B-2 Flanges.

HASTELLOY C276 is not prone to grain boundary precipitation in the as welded condition and therefore suitable for many chemical process applications.

HASTELLOY X pipe bend is a wrought nickel base alloy with excellent high temperature strength and oxidation resistance. All of the product forms are excellent in terms of forming and welding.

Hastelloy B3 Threaded Flange (UNS N10675) has great resistance to knife ¨C line and heat ¨C affected zone attack. Hastelloy B3 Slip On Flange has a special chemistry designed to achieve greater thermal stability than B-2 alloy, resulting in easier fabrication. Hastelloy B3 Spectacle Blind Flanges have good creep and oxidation resistance.

Alloy C-276 also has excellent resistance to pitting, stress-corrosion cracking and oxidizing atmospheres up to 1900¡ãF. Alloy C-276 has exceptional resistance to a wide variety of chemical environments.

Hastelloy B-3 is a nickel-molybdenum alloy with excellent resistance to pitting, corrosion, and stress-corrosion cracking plus, thermal stability superior to that of alloy B-2. In addition, this nickel steel alloy has great resistance to knife-line and heat¨Caffected zone attack.

Alloy C-276 has excellent resistance to pitting corrosion, stress corrosion cracking and oxidizing atmospheres up to 1900¡ãF.

The flange is second most used joining method after selding. Flanges are used when joints need dismantling. It provides flexibility for maintenance. Flange connects the pipe with various equipment and valves. Breakup flanges are added in the pipeline system if regular maintenance in required during plant operation.
A flanged joint is composed of three separate and independent although interrdlated components; the flanges, the gaskets, and the bolting; which are assembled by yet another influence, the fitter. Special controls are required in the selection and application of all there elements to attain a joint, which has acceptable leak tightness.
A flange is a protruded ridge, lip or rim, either external or internal, that serves to increase strength (as the flange of an iron beam such as an I-beam or a T-beam); for easy attachment/transfer of contact force with another object (as the flange on the end of a pipe, steam cylinder, etc., or on the lens mount of a camera); or for stabilizing and guiding the movements of a machine or its parts (as the inside flange of a rail car or tram wheel, which keep the wheels from running off the rails). The term “flange” is also used for a kind of tool used to form flanges.

C22 is typically provided in the annealed condition with a minimum yield strength of 45 ksi. However, C22 can be cold worked to higher strength levels.

Applications in air pollution control include stack liners, ducts, dampers, scrubbers, stack-gas re-heaters, fans and fan housings.

Superior resistance to hydrochloric acid, aluminum chloride catalysts and other strongly reducing chemicals. Excellent high-temperature strength in inert and vacuum atmospheres.

The use of modular construction is directly influenced by the client¡¯s requirements for speed of construction, quality, added benefits of economy of scale, as well as single-point procurement.

Hastelloy C22, also known as Alloy C22, is a general-purpose austenitic grade alloy. The primary alloy materials used in Hastelloy C22 fasteners include metals such as nickel, chromium, molybdenum and tungsten. The main characteristic or characteristic of Hastelloy WERKSTOFF NR. 2.4602 Bolts are their enhanced resistance to pitting, crevice corrosion, and stress-related corrosion cracking.

Hastelloy Alloys Directory
The Corrosion Resistant HASTELLOY alloys are widely used by the chemical processing industries. The need for reliable performance leads to their acceptance and growth in the areas of energy, health and environmental, oil and gas, pharmaceutical and flue gas desulfurization industries.

Hastelloy B3 is a nickel-molybdenum alloy with profound resistance to stree-corrosion cracking, pitting, corrosion and thermal stability greater to that of alloy B2.

Hastelloy C22 alloy includes nickel, chromium, molybdenum, and tungsten, which result in extreme resistance to pitting and stress corrosion cracking.

Thus these Hastelloy B2 Flanges are considered to be well suited to be used for most chemical process applications in an as-welded condition. Due to lower carbon content in the alloy, there is reduced precipitation of carbides as well as other phases in the heat-affected weld zones, which in turn ensures uniform resistance to corrosion in the flange.

The 2.4819 Alloy C276 Flat Plate is typically used in areas with extreme conditions.

Hastelloy C22 Flanges are a technique used by many industries in the connecting of pipes, valves, pumps and other equipment, into what is referred to as a piping system.

La aleacion tambien es resistente a soluciones y compuestos de cloruro, muchos de los cuales son altamente corrosivos. Por ejemplo, los reductores de aleacion de niquel C276 son resistentes no solo a los medios organicos e inorganicos termicamente contaminados, sino tambien a los cloruros ferricos y c¨²pricos, asi como al cloro, el agua de mar y la salmuera.

C22 has excellent resistance to oxidation, carburization, and sulfidation at elevated temperatures. However, C22 should not be used at temperatures above 1250¡ãF due to the possible formation of embrittling phases.

This nickel steel alloy has good resistance to heat affected and knife-line zone attack. This alloy also bears the brunt of formic, sulfuric, phosphoric, acetic acids and various other non-oxidizing media.

C-276 alloy has excellent resistance to pitting and to stress-corrosion cracking. It is also one of the few materials that withstands the corrosive effects of wet chlorine gas, hypochlorite, and chlorine dioxide.

The flange is second most used joining method after selding. Flanges are used when joints need dismantling. It provides flexibility for maintenance. Flange connects the pipe with various equipment and valves. Breakup flanges are added in the pipeline system if regular maintenance in required during plant operation.
A flanged joint is composed of three separate and independent although interrdlated components; the flanges, the gaskets, and the bolting; which are assembled by yet another influence, the fitter. Special controls are required in the selection and application of all there elements to attain a joint, which has acceptable leak tightness.
A flange is a protruded ridge, lip or rim, either external or internal, that serves to increase strength (as the flange of an iron beam such as an I-beam or a T-beam); for easy attachment/transfer of contact force with another object (as the flange on the end of a pipe, steam cylinder, etc., or on the lens mount of a camera); or for stabilizing and guiding the movements of a machine or its parts (as the inside flange of a rail car or tram wheel, which keep the wheels from running off the rails). The term “flange” is also used for a kind of tool used to form flanges.

Strong and Oxidation Resistant to 2200 Deg. F (1200 Deg. C) – HASTELLOY X pipe bend is a solid solution strengthened grade has good strength and oxidation resistance up to 2200 Deg. F (1200 Deg. C).

The high nickel and molybdenum contents make the nickel steel alloy especially resistant to pitting and crevice corrosion in reducing environments while chromium conveys resistance to oxidizing media.

Although Alloy C276 plate has a higher rate of work hardening compared to its austenitic counterpart, in-process annealing may be required if nickel alloy C276 plate is to be work hardened to a higher degree. Solution annealing may be required if the deformation of the nickel C276 strip exceeds 15%.