Monel 400 UNS N04400 Tube bending particularly resistant to hydrochloric and hydrofluoric acids when they are de-aerated

SCH40 Monel 400 Pipe is designated as Werkstoff Number 2.4360 and UNS N04400. Alloy 400 Pipe also known as Monel Alloy 400 Pipe, Monel 400 Pipe & Nickel Alloy 400 Pipe.

Nickel Alloy 400 and Monel 400, also known as UNS N04400, is a ductile nickel-copper-based alloy consisting primarily of two-thirds nickel and one-third copper. Nickel Alloy 400 is known for its resistance to a variety of corrosive conditions, including alkalis (or acids), salt water, hydrofluoric acid, and sulfuric acid. Since Monel 400 or Alloy 400 is a cold worked metal, this alloy has high hardness, stiffness and strength. By cold working ASTM B164 UNS N04400 bar stock, the alloy is subjected to higher levels of mechanical stress, which in turn causes changes in the alloy’s microstructure.

Nickel-copper-based alloy 400 Monel 2.4360 cold drawn rod is virtually immune to chloride stress-related corrosion cracking when exposed to corrosive media in typical environments. Monel 400 is a copper and nickel based alloy that is popular today due to its high performance. The alloy has excellent acid and alkali resistance. In addition, it has good tensile strength, ductility, excellent thermal conductivity, and can be hardened by cold work. Additionally, it can be used in applications with temperatures ranging from minus to 538 degrees Celsius.

ASME Sb564 Alloy 400 Plate Flanges Monel 400 N04400 Orifice Flange the Monel 400 Flanges shows evidence of excellent temperature. On the other hand, properties such as Strength and hardness of the Monel 400 Lap Joint Flange is only slightly diminished with regards to the other properties like ductility or impact resistance.

ALLOY400 is a single-phase solid-solution Ni-Cu alloy with excellent corrosion resistance to a wide range of media.

The increased properties are obtained by adding aluminum and titanimum to the nickel-copper base, and by heating under controlled conditions so that submicroscopic particles of Ni3 (Ti, Al) are precipitated thoughout the matrix.

Monel 400 is used in process vessels, heat exchanger piping, and gasoline and potable water storage tanks in the marine sector. The non-sparking properties of this alloy make it suitable for high-risk situations in the explosives industry, rockets and pulp and paper industries.

At room temperature settings, Monel 400 exhibits slight magnetic behavior, thus, the use of WNR 2.4360 Reducing Flange could also be extended to applications that require magnetic characteristics to a certain degree.

ALLOY400 is a single-phase solid-solution Ni-Cu alloy with excellent corrosion resistance in a wide range of marine and chemical environments and has freedom from chloride induced stress-corrosion cracking.

Alloy 400 (UNS N04400) is a nickel copper alloy with high strength (comparable to structural steel) and toughness. Alloy 400 also has excellent corrosion resistance in a range of media including seawater, hydrofluoric acid, sulphuric acid and alkalis.

Generally, the corrosion resistance of Monel K500 in solid solution is basically the same as that of Monel 400 alloy, so the corrosion resistance data of Monel 400 can be applied to Monel K500 alloy. Due to its low corrosion rate and high strength in flowing seawater, the alloy is particularly suitable for manufacturing seawater corrosion-resistant centrifugal pump shafts.

Monel 400 and K500 flanges also exhibit excellent corrosion resistance in marine applications and have reasonable corrosion resistance to sulfuric and hydrochloric acids under reducing conditions.

Known for their improved workability under cryogenic temperatures, with a rigidity of 160 ksi and a superb dimensional security are variables that add to the unwavering quality of UNS N05500 Monel K500 Socket Weld Flanges. The ASTM B564 Monel 400 Lap Joint Flanges and other flanges can also come as threaded, forged, screwed or plate flange types.

Monel 400 is corrosion resistant to most salts, water, alkalis, organic substances, food products, and atmospheric conditions at both normal and elevated temperatures.

Monel400 Copper-nickel alloy (UNSN04400) is a soft Copper-nickel alloy that is resistant to various corrosive environments.

Monel K500 fasteners are cold worked prior to precipitation hardening. The strength of the fasteners is stable to 1200 degrees Fahrenheit. Here, at this temperature, it becomes more ductile, reaching toughness around 400 degrees Fahrenheit. Higher strength and hardness after precipitation hardening compared to 400. Due to its numerous advantages, Monel K500 ASTM fasteners are used in a wide range of industries.

Alloy 400 is a nickel copper solid solution strengthened alloy. The alloy is characterized by moderate strength, good weldability, good general corrosion resistance and good toughness.

Monel 400 flanges are a nickel-copper alloy (approximately 67% Ni ¨C 23% Cu) resistant to seawater and steam at high temperatures, as well as salt and caustic solutions. Alloy 400 is a solid solution alloy that can only be hardened by cold work. This nickel alloy has good corrosion resistance, good weldability and high strength.

Alloy K500 has approximately three (3) times the yield strength and double the tensile strength when compared with 400. MONEL K500 can be further strengthened by cold working before the precipitation hardening.

Monel k500 has good corrosion resistance and long-term organizational stability.

Monel 400 operates in a wide range of acidic and alkaline environments and has excellent ductility and thermal conductivity. Its properties make it ideal for heavy-duty applications and those requiring a high melting point and toughness in the harshest conditions.

Alloy 400 is a solid solution of gold that can only be hardened by cold work.

ALLOY400 is a single-phase solid-solution Ni-Cu alloy with good mechanical properties from sub-zero temperatures up to about 550 ¡ãC (1020 ¡ãF) and is approved for pressure vessels with wall temperatures from -10 to 425 ¡ãC (14 to 800 ¡ãF) according to VdTUV-Wbl. 263 and up to 900 ¡ãF (480 ¡ãC) according to ASME Boiler and Pressure Vessel Code.

The Monel K500 flanges available in our company are customized in designs, sizes and shapes. The specification of these flanges is ASTM B564. These flanges range in size from 1/8 inches to 48 inches.

Applications that deal with the marine environment are required to be resilient to the effects of saltwater. After all, the concentration of salt in marine water is about 3.5%, enough to corrode ordinary steels with no protective surface treatment.

The chemical composition of Monel K500 Nippo Flanges provides great resistance to a lot of corrosive environments, such as pitting, crevice corrosion, inter ¨C granular corrosion, and stress ¨C corrosion cracking. Monel K500 Spacer Flanges has useful resistance to boiling sulfuric acid up to 40 % concentration, to 60 % concentration at 176 Degree F and in all concentrations to 150 Degree F.

MONEL 400 solid solution alloy can be hardened by cold work, but can be hot worked or cold worked, then annealed into complex structures and welded using an appropriate welding process.

These Flanges are widely used in various application industries such as petroleum, chemical, construction, engineering, gas and shipbuilding industries and many more.

The corrosion resistance of Monel K500 Weld Neck Flanges is substantially equivalent to that of alloy 400 Weld Neck Flanges except that, when in the age ¨C hardened condition, it has a greater tendency toward stress ¨C corrosion cracking in some environments.

Monel 400 Bolts and Nuts are made from a nickel-copper alloy for extreme corrosion resistance, especially in sour conditions. The material is also strong and rigid and can be used to produce bolts and nuts for high temperature service. HT PIPE is a leading manufacturer and supplier of Monel 400 Bolts and Nuts of all sizes and types. Among the ingredients are carbon, aluminum, manganese, silicon, iron, sulfur and 63% nickel and 28% copper. This composition gives the material a high melting point.

It has a higher melting point around 2400 degrees Fahrenheit to 2460 degrees Fahrenheit. Primarily Monel K500 grade is a spark resistant alloy. This becomes non-magnetic below -200 degrees Fahrenheit. In terms of cold working operations, magnetic structures can be achieved. The Monel nickel-copper composition of Monel 500 is highly resistant to corrosion, making it ideal for many types of industrial applications that require extreme environmental protection, such as salt water and strongly acidic conditions.

The alloy has great mechanical properties at subzero temperatures, and with a melting point of 2370¡ã ¨C 2460¡ã F, products can be used at temperatures up to 1000¡ã C.

Both sulfuric acid as well as hydrofluoric acid are highly corrosive solutions and can easily corrode metals, without good resistance to reductive agents.