special-shaped flange A182 F11 flange ideally used in pipes

Common Trade Names: Nickel Alloy 36, Invar 36®, Nilo 6®, Pernifer 6®
Invar 36® is a nickel-iron, low expansion alloy that contains 36% nickel, Invar 36 has a low coefficient of expansion from cryogenic temperatures to about +500°F (260°C).
Invar 36 Tube OD:0.2-6mm, WT: 0.02-2mm

Nilo / Alloy K W.Nr.: 1.3981
UNS: K94610 ASTM F15
Fixed-expansion glass-encapsulated iron-nickel-cobalt alloys, Kovar alloys, have a linear thermal expansion coefficient similar to that of hard glass within a certain temperature range
For mating sealing with hard glass

Nilo Alloy 36, W.Nr 1.3912, Invar 36® is a nickel-iron, low controlled expansion alloy that contains 36% nickel and possesses a rate of thermal expansion approximately one-tenth that of carbon steel.
Invar 36 Specifications: UNS K93600, W.Nr 1.3912

Bolts and bolts are used in many applications in almost all industrial applications.

ASTM A182 Grade F5 Flanges are suitable for connecting pipes of small bore size and without the requirement of welding. ASTM A182 GR F5 Flange belongs to the ASTM A182 specification. The dimensions of the flanges vary according to the ANSI, ASME and DIN standards. The flange sizes range from ? inches to 36 inches in nominal bore sizes. Navstar Steel is a leading supplier and manufacturer of these flanges in various sizes and types.

ASME SA182 F5 pipe flange weight depends on wall thickness and nominal bore. The wall thickness of the flange is determined by the pressure rating.

This ASTM A182 alloy steel flange has a smaller thickness for easier placement of bolt holes. These ASTM A182 F12 alloy steel pipe flanges are suitable for high temperature and high pressure environments.

The provided Alloy Steel F21 Flange are efficiently manufactured using the superior quality nickel alloy with the aid of pioneering methodology.

A182 grade is an excellent alloy that is hardened only by cold work. Commonly used in nuclear energy, medical equipment, chemical energy, etc.

Alloy Steel F12 Flanges are made up of a chromium molybdenum alloy consisting chromium in a range of 20% to 40% depending on the grading. Also, for Alloy Steel F12 Flanges, there several excellent properties the product is having that is making it the best choice for various critical applications.

ASTM A335 is the standard specification for seamless ferritic alloy steel pipe for high temperature service. Covers server levels: P1, P2, P5, P5b, P5c, P9, P11, P12, P15, P21, P22, P23, P91, P92, P122, of which P5, P9, P11, P22, P91, P92 are used in practice the most extensive. This specification covers nominal and minimum wall chrome-molybdenum (also known as Cr-Mo or Cr-Moly) alloy steel pipes for high temperature applications. Pipe ordered to this specification shall be suitable for bending, vanstoning and similar forming operations, and fusion welding. ASTM A335 P11, P22, P91 and P92 are commonly used in power plants and the chemical and petrochemical industries, while P9 and P5 are mainly used in oil refineries.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.19
Material Alloy Steel ASTM A333 Grade 3, Grade 6,Grade 8,Grade 9
ASTM A335 P5,P9,P11,P12,P22,P91,P106

The ease and economy with which INCONEL alloy 718
can be fabricated, combined with good tensile, fatigue,
creep, and rupture strength, have resulted in its use in a
wide range of applications.

Due to its ease of welding, ASTM A335 Grade P91 Welded Pipe can be welded well into piping systems. Pipes have different tolerance classes and test standards depending on the application requirements, grade, schedule and pressure rating of the pipe material.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.28

Chrome alloy steel flanges are manufactured in accordance with ASTM A182 F11/F12 and are widely used in nuclear power plants, power plants, water systems, electric power, oil fields, pipeline engineering, natural gas, marine engineering, shipbuilding and other industries. These flanges are harder and stronger than regular steel, but not as corrosion resistant as stainless steel.

The austenitic formation of Alloy Steel F9 Weld Neck Flanges offers outstanding durability, even at cryogenic temp. Those are high tensile strength, anti-corrosive, flexibility, durability, low maintenance, good dimensional accuracy, excellent surface finishes.

The ASTM A194 specification covers a wide variety of carbon, alloy, and martensitic stainless steel nuts in sizes ranging from 1/4 to 4 inches and metric M6 to M100 nominal. It also covers austenitic stainless steel nuts in the size range of 1/4 inch and M6 nominal and above. These nuts are used for high pressure or high temperature service, or both.

A193 B7 Cadmium Plated stud bolts are made of alloy steel for high temperature environments. ASTM standards cover alloy steel and stainless steel bolting materials; this specification covers fasteners for pressure vessels, valves, flanges, and fittings.

It is the addition of other elements that make alloy steel stronger. Heat-treated elements such as silicon and manganese give alloy steels improved properties and additional benefits, such as increased corrosion resistance or improved weldability.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.49

The specification for ASTM A320 Grade L7m materials covers alloy steel and stainless steel bolting materials for low temperature applications. ASTM A320 L7 Studs can also be used in applications with ambient temperatures up to -150oF. ASTM A320 grade L7m bolts and ASTM A320 bolts have a minimum Charpy impact value of 15 foot-pounds at this temperature.

The carbon content of 4140 alloy steel pipe is 0.38-0.43%, the manganese content is 0.75-1.00%, the phosphorus content is 0.04%, the sulfur content is 0.04%, the silicon content is 0.15-0.35%, the chromium content is 0.8-1.10%, and the molybdenum content is 0.8-1.10%. is 0.15-0.25 % maximum in its composition. The material can be heat treated to anneal and normalize in air, or quench and temper in polymer or oil.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.19
Material Alloy Steel ASTM A333 Grade 3, Grade 6,Grade 8,Grade 9
ASTM A335 P5,P9,P11,P12,P22,P91,P138

Chromium molybdenum has a better strength-to-weight ratio than steel, which enables designers to use thinner walled tubing or smaller diameter tubing to reduce overall weight.

Our alloy steel pipes are available in different sizes, grades, gauges and thicknesses according to customer’s custom requirements. We also supply these alloy steel LSAW pipes to our valuable customers at fairly reasonable prices.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.19

Alloy Steel F12 slip on Flanges are made up of chromium molybdenum steel alloy and therefore have a high rupture resistance. They are also preferred due to their light weight because of the low carbon and high alloy nature.Alloy Steel ASTM A182 flanges are very simple to install and have a low center because the pipe occasionally trips into the flanges after welding.

ASTM A182 F5 flanges are forged flanges made of chrome molybdenum low alloy steel called 5Cr-0.5Mo, UNS designation K41545. Widely used in oil refineries, chemical and petrochemical, power plant pipelines, heat exchangers, various pressure vessels and other pressure and high temperature services.

A320 Gr L7 studs are subject to certain mandatory mechanical tests, namely: tensile test, impact test and hardness test.

Commercially pure wrought Nickel with good mechanical properties over a wide range of temperature and excellent resistance to many corrosives, in particular hydroxides.

Good resistance to corrosion in acids and alkalis and is most useful under reducing conditions. Outstanding resistance to caustic alkalis up to and including the molten state. In acid, alkaline and neutral salt solutions the material shows good resistance, but in oxidizing salt solutions severe attack will occur. Resistant to all dry gases at room temperature and in dry chlorine and hydrogen chloride may be used in temperatures up to 550C. Resistance to mineral acids varies according to temperature and concentration and whether the solution is aerated or not. Corrosion resistance is better in de aerated acid.

There are different schedules for P91 metal piping materials, corresponding to different pressure classes. sa335 P91 seamless pipe can withstand high pressure and high temperature and can also be welded to other pipes and fittings.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.27

Chromium-molybdenum alloy steel has strong crack resistance under high temperature and high pressure. Chromium molybdenum is also resistant to hydrogen attack and hot sulfide corrosion cracking.

B7 and B7M shall be heat treated by quenching in a liquid medium and tempering. For B7M fasteners, the final heat treatment, which may be the tempering operation if conducted at 1150 ¡ãF [620 ¡ãC] minimum, shall be done after all machining and forming operations, including thread rolling and any type of cutting.

A335 gr P22 seamless pipe is easy to install as the dimensions are very accurate. It can be used with other a335 gr P22 alloy pipe types and fittings.
Type Seamless Pipe
Seamless Tube
Welded Pipe
Welded Tube
SAW LSAW ERW EFW
Beveled End, Plain End”
Size OD: 1/2″” ~48″”
Thickness: SCH5~SCHXXS
Length :As per your requirement.”
Manufacturing technique Hot rolling /Hot work ,Cold rolling
Producing Standard ASME B36.10 ASME B36.40

Blind flanges have the face thickness of a flange, a matching face type, and similar bolting pattern.

Alloy steel is steel that is alloyed with a variety of elements in total amounts between 1.0% and 50% by weight to improve its mechanical properties. Alloy steels are broken down into two groups: low alloy steels and high alloy steels. The difference between the two is disputed. Smith and Hashemi define the difference at 4.0%, while Degarmo, et al., define it at 8.0%.[1][2] Most commonly, the phrase “alloy steel” refers to low-alloy steels.

Alloy steel is steel that is alloyed with a variety of elements in total amounts between 1.0% and 50% by weight to improve its mechanical properties. Alloy steels are broken down into two groups: low alloy steels and high alloy steels. The difference between the two is disputed. Smith and Hashemi define the difference at 4.0%, while Degarmo, et al., define it at 8.0%.[1][2] Most commonly, the phrase “alloy steel” refers to low-alloy steels.