Under alternating oxidizing and reducing conditions, alloys may suffer from selective oxidation.

The alloy is also resistant to ammonia-containing atmospheres as well as nitrogen and carburizing gases.

Inconel 600 is non-magnetic, has excellent mechanical properties, combines high strength with good workability, and is easy to weld. Alloy 600 exhibits cold forming properties typically associated with chromium-nickel stainless steels.

Alloy 600 is not an age hardening alloy; cold working is the only hardening method available.

Annealing softening begins at approximately 1600¡ãF (871¡ãC) and is fairly complete after 10 to 15 minutes of heating at 1800¡ãF (982¡ãC). Above this temperature, grain growth can be objectionable, although very brief heating at 1900¡ãF will result in complete softening without excessive grain growth. Since the cooling rate has no effect on softening, the material can be water quenched or air cooled.

Alloy 600 is machinable in both hot and annealed conditions. Due to the large amount of heat generated when machining this alloy, high-speed steel, cast non-ferrous or carbide tools should be used.

Alloy 600’s high chromium content makes it significantly more resistant to oxidation than pure nickel, while its high nickel content provides good corrosion resistance under reducing conditions.
This alloy has a high level of resistance to stress and salt water, exhaust gases, and most organic acids and compounds.

At elevated temperatures, the annealed and solution annealed alloys exhibit good oxidation resistance and high strength.

Alloy 600 is relatively immune to most neutral and alkaline salt solutions and is used in some corrosive environments. The alloy is resistant to steam and mixtures of steam, air and carbon dioxide.

Its typical corrosion applications include titanium dioxide production (chloride route), perchloroethylene synthesis, vinyl chloride monomer (VCM) and magnesium chloride. Alloy 600 is used in chemical and food processing, heat treatment, phenol condensers, soap making, vegetable and fatty acid containers, and more.

Resistant to various corrosive media. Chromium content provides better resistance in oxidizing conditions than alloys 200 and 201, while high nickel provides good resistance in reducing conditions.

It is virtually immune to chloride ion stress corrosion cracking. Sufficient resistance to organic acids such as acetic acid, formic acid and stearic acid.

Little or no corrosion occurs in dry gases such as chlorine or hydrogen chloride at room temperature and high temperature. At temperatures up to 550C in these media, this alloy has proven to be one of the most corrosion resistant common alloys.

This alloy is approximately 2 times stronger than Inconel 625, has excellent creep rupture strength at temperatures up to 1300¡ãF (700¡ãC), and can be used at temperatures up to 1800¡ãF (982¡ãC).

Inconel 718 is a versatile, high-strength nickel-based superalloy for cryogenic applications up to and beyond 1000 degrees Fahrenheit. It has very high yield strength, tensile strength and creep rupture properties.

Inconel 718 flanges are the highest quality finishing fittings for long life, high pressure and zero defects. Inconel 718 flanges are alloys that maintain strength, toughness and corrosion resistance in high temperature environments. These alloys are used in a variety of industries and valuable applications such as oil refineries, chemical plants and power generation, nuclear power, aerospace and more.

The added titanium, with proper heat treatment, stabilizes the susceptibility of Inconel plate flanges to intergranular corrosion. With an unwavering commitment to quality, we offer our customers a wide variety of Inconel Butt Weld Neck Raised Face Flanges.

Inconel 718 flanges have excellent mechanical properties over a wide temperature range. These Inconel 718 flanges have high creep rupture strength at elevated temperatures up to approximately 700 degrees Celsius (1290 degrees Fahrenheit). Our Inconel 718 flanges combine corrosion resistance and high strength with excellent weldability, including resistance to post weld cracking.

In addition to basic alloys, our flanges are available in titanium, aluminum, cobalt, boron, copper, iron and other metals. Inconel 718 flanges offer uncompromising protection against oxidation and corrosion factors.

Inconel 718 alloy is also used in industries such as oil and gas drilling and production due to its high tensile strength and good corrosion resistance to chloride-related stress cracking and sulfide-related stress cracking. In these industries, Ams 5663 material has been used to manufacture various parts such as valves, pump shafts and wellhead components.

Inconel 718 flanges are also ideal for a variety of applications in industry due to their purity and strength. Inconel 718 Socket Weld Flanges are used for hot extrusion dies, pump bodies and parts, etc. Inconel 718 lap flanges account for 50% of the world’s tonnage.

Werkstoff Nr 2.4668 forged parts can be easily machined in the annealed or age hardened condition. While machining the alloy in the age hardened condition yields a better surface finish, machining Inconel 718 alloy in the annealed condition yields longer tool life.

Inconel flanges are constructed of high-grade 718 material for optimum heat and corrosion resistance properties. These flanges have excellent dimensional accuracy and excellent surface finish.

Inconel 718 contains nickel, chromium and molybdenum alloys as well as aluminum, niobium and titanium elements and is suitable for flange manufacturing. Our premium flanges have excellent yield strength and tensile strength. Our premium flanges also offer excellent resistance to corrosion, crevice corrosion, pitting and oxidation in severely corrosive environments. Has excellent workability, weldability and machinability,

Inconel UNS N06601 Pipe Flanges Inconel 601 is a nickel-chromium alloy used for applications that require resistance to corrosion and heat. This nickel alloy stands out due to its resistance to high temperature oxidation, remaining highly resistant to oxidation through 2200¡ã F. Alloy 601 develops a tightly adherent oxide scale which resists spalling even under conditions of severe thermal cycling.

Inconel UNS N06601 LWN Flanges nconel 601 is a nickel-chromium alloy used for applications that require resistance to corrosion and heat. This nickel alloy stands out due to its resistance to high temperature oxidation, remaining highly resistant to oxidation through 2200¡ã F. Alloy 601 develops a tightly adherent oxide scale which resists spalling even under conditions of severe thermal cycling.

ASTM B564 Uns N06600 Flanges nconel 601 is a nickel-chromium alloy used for applications that require resistance to corrosion and heat. This nickel alloy stands out due to its resistance to high temperature oxidation, remaining highly resistant to oxidation through 2200¡ã F. Alloy 601 develops a tightly adherent oxide scale which resists spalling even under conditions of severe thermal cycling.

INCONEL 601 Welding Neck Flanges Inconel 601 is a nickel-chromium alloy used for applications that require resistance to corrosion and heat. This nickel alloy stands out due to its resistance to high temperature oxidation, remaining highly resistant to oxidation through 2200¡ã F. Alloy 601 develops a tightly adherent oxide scale which resists spalling even under conditions of severe thermal cycling.

Inconel UNS N06601 Pipe Flanges Inconel 601 is a nickel-chromium alloy used for applications that require resistance to corrosion and heat. This nickel alloy stands out due to its resistance to high temperature oxidation, remaining highly resistant to oxidation through 2200¡ã F. Alloy 601 develops a tightly adherent oxide scale which resists spalling even under conditions of severe thermal cycling.

Inconel UNS N06601 LWN Flanges nconel 601 is a nickel-chromium alloy used for applications that require resistance to corrosion and heat. This nickel alloy stands out due to its resistance to high temperature oxidation, remaining highly resistant to oxidation through 2200¡ã F. Alloy 601 develops a tightly adherent oxide scale which resists spalling even under conditions of severe thermal cycling.