ASTM A350 LF2 low temperature alloy steel round bar rode carbon steel
There is an extra low carbon version in ASTM A350 LF2 LT Carbon Steel Rods, where the lower carbon content minimizes deleterious carbide precipitation as a result welding. ASME SA 350 LF2 LTCS Bars is used when welding is required in order to ensure maximum corrosion resistance. ASME SA 350 LF2 LTCS Rods is used in furnace parts, heat exchangers, jet engine parts, pharmaceutical etc. ASTM A350 LTCS LF2 Round Bars is a titanium stabilized version of molybdenum bearing austenitic stainless steel. ASTM A350 LTCS LF2 Bars have properties such as toughness, durability, corrosion resistance, high temperature & creep.
Low Temperature Carbon Steel Round Rods, Bars Specification
| Specifications |
ASTM A350 / ASME SA350 |
| Standards |
EN, DIN, JIS, ASTM, BS, ASME, API, GB, AISI |
| Range |
5 mm To 500 mm thick in 100 mm TO 6000 mm Length available with NACE MR 01-75. |
| Length |
1 to 6 Meters, Custom Cut Lengths 12M |
| Form |
Round, Square, Hex (A/F), Rectangle, Wire (Coil Form), Wire-mesh, Billet, Ingot, Forging Etc. |
| Condition |
Cold Drawnd Pulished Cold Drawn Centreless Ground & Polished, Annealed round bar |
| Finish |
Grinding, Bright, Bright, Polish, Centreless Ground & Black, Rough Turned |
ASME SA350 LF2 Carbon Steel Round Bar and Rod Chemical Composition
| Grade |
C |
Si |
Mn |
P |
S |
Cr |
Mo |
Cu |
Nb |
V |
| A350 LF2 |
≤0.30% |
0.15 – 0.30% |
0.60 – 1.35% |
≤0.035% |
≤0.040% |
≤0.30 % |
≤0.12% |
≤0.40% |
≤0.02% |
≤0.08% |
Carbon Steel ASTM A350 LF2 Round Bars Mechanical Properties
| Grade |
Tensile strength, (MPa) |
Yield (0.2%) (MPa) |
Elongation (%) |
Reduction of Area (%) |
Hardness HB |
| LTCS LF2 |
485-655(70-95KSi) |
250(36KSi) |
22 |
30 |
≤197HB |
Qualities of the product-
All our manufactured ranges of ASTM A350 LF2 Carbon Steel Bars are having many good qualities. These excellent qualities have led us to make use of the product in several industries. The qualities found in our bars are mentioned herein-
• Good tensile strength
• Longevity
• Rust resistance
• Non-corrosive body
• Pure in nature
• Withstands high temperature
• Withstands heavy loads
• Good mechanical properties
• General corrosion resistance
• Stress corrosion cracking and crevice corrosion resistance
Bars testing by us-
We at our highly operational manufacturing unit are conducting the testing of the produced material for the purpose of quality checking. The tests done are by the quality checker team and keeping in mind a few set parameters. The tests done are namely-
• Radiography test
• Hardness test
• Pitting resistance test
• Macro test
• Positive material identification test
• Intergranular corrosion test
• Micro test
• Chemical test
• Mechanical test
• bend and impact test