Incoloy 800H(UNS N08810, 1.4958, 1.4876) has good creep-rupture properties at temperatures above 1100°F (600°C). It remains ductile during long term use at temperatures below 1290°F (700°C) due to a maximum titanium and aluminum content of 0.7%. Alloy 800 with a standard anneal is recommended for service below 1100°F (600°C). Alloy 800H resists reducing, oxidizing and nitriding atmospheres, as well as, atmospheres that alternate between reducing and oxidizing. The alloy remains stable in long term high temperature service.
HT PIPE provide Incoloy 800H Seamless and Welded Pipes for the Oil and Gas, Petrochemical and Power Industries. Incoloy pipes supplier in China. ASTM B407 Incoloy 800H Seamless pipe, Incoloy 800H Seamless tube, 1.4958 Incoloy Seamless pipe, 1.4876 Seamless tube, 1.4876 seamless pipe and tube supplier, exporter.
Alloy 800H has the following properties:
1. Excellent corrosion resistance in extremely high temperature aqueous media up to 500°C
2. Good resistance to stress corrosion
3. Good workability
Metallographic structure of Incoloy 800H:
800H is a face-centered cubic lattice structure. Very low carbon content and increased Ti:C ratio increase structural stability and maximum resistance to sensitization and intergranular corrosion. A low-temperature annealing around 950°C ensures a fine-grained structure.
Corrosion resistance of Incoloy 800H:
800H can resist corrosion of many corrosive media. Its high nickel content makes it resistant to stress corrosion cracking in aqueous corrosion conditions. The high chromium content provides better resistance to pitting and crevice corrosion cracking. The alloy has good corrosion resistance to nitric acid and organic acids, but limited corrosion resistance in sulfuric acid and hydrochloric acid. Good corrosion resistance in oxidizing and non-oxidizing salts, in addition to the potential for pitting corrosion in halides. It also has good corrosion resistance in water, steam and mixtures of steam, air and carbon dioxide.
The Chemical Composition of Incoloy 800H, %
| Ni |
Cr |
Fe |
Ti |
Al |
C |
Mn |
P |
Si |
S |
Al & Ti |
| 30.0-35.0 |
19.0-23.0 |
39.5 |
0.15-0.60 |
0.15-0.60 |
0.05-0.10 |
1.5 |
0.045 |
1 |
0.015 |
0.30-1.20 |
Physical Properties of Incoloy 800H
Density: 8.0 g/cm3
Melting point: 1350-1400 ℃
Incoloy 800H Pipe Mechanical Properties
| Mechanical properties |
Tensile, min, ksi[MPa] |
Yield, min, ksi[MPa] |
Elongation, %(min) |
| Incoloy 800H |
65[450] |
25[170] |
30 |
Incoloy 800H Pipe Equivalent Grades
| STANDARD |
WERKSTOFFNR. |
UNS |
JIS |
BS |
GOST |
AFNOR |
EN |
OR |
| Incoloy 800H |
1.4958 / 1.4876 |
N08810 |
NCF 800H |
NA 15(H) |
ЭИ670 |
Z8NC33-21 |
X5NiCrAlTi31-20 |
XH32T |